Moisture-Dependent Transverse Isotropic Elastic Constants of Wood S2 Secondary Cell Wall Layers Determined Using Nanoindentation

Abstract

Moisture- and orientation-dependent mechanical properties of the S2 secondary cell wall layer are needed to better understand wood mechanical properties and advance wood utilization. In this work, nanoindentation was used to assess the orientation-dependent elastic moduli and Meyer hardness of the loblolly pine (Pinus taeda) S2 layer under environmental conditions ranging from 0% to 94% relative humidity (RH). The elastic moduli were fit to a theoretical transverse isotropic elasticity model to calculate the longitudinal elastic modulus, transverse elastic modulus, axial shear modulus, and transverse shear modulus for the S2 layer at 0%, 33%, 75%, and 94% RH and 26 ◦C. The longitudinal elastic modulus was consistently higher than the transverse elastic modulus because of the orientation of the stiff cellulose microfibrils in the S2 layer. The axial shear modulus was consistently higher than the transverse shear modulus. The Meyer hardness had a much smaller orientation dependence than the elastic properties. Moisture generally plasticized the S2 layer. Over the range of RH tested, the longitudinal elastic modulus decreased by 30%, the transverse elastic modulus and transverse shear modulus decreased by 83%, the axial shear modulus did not have an observable trend with RH, and the hardness decreased by 68% to 82% with the hardness in the longitudinal direction softening less than in the transverse direction.

Citation

Arzola-Villegas, Xavier; Plaza, Nayomi Z.; Bechle, Nathan J.; Wang, Yikai; Lakes, Roderic; Stone, Donald S.; Jakes, Joseph E. 2025. Moisture-Dependent Transverse Isotropic Elastic Constants of Wood S2 Secondary Cell Wall Layers Determined Using Nanoindentation. Forests. 16: 712. 27 p. https://doi.org/10.3390/f16050712.